PRODUCT CATALOG
Polyvinyl alcohol (PVA) is a water-soluble resin formed by polymerization and alcoholysis of ethylene. It has unique strong adhesion, tough film formation, smoothness, oil resistance, solvent resistance, gas resistance, and wear resistance, and can be made water-resistant through special treatment.
Taiwan CCP PVA applications in adhesives include (1) construction adhesives; (2) polyvinyl acetate white latex.
| Grade | Viscosity (cps) | Hydrolysis (mole %) | Volatile (wt%) | Ash (wt%) | pH | Application |
|---|---|---|---|---|---|---|
| BP-28 | 60-70 | 86-89 | <5 | <0.5 | 5-7 | Adhesive,remoistenable adhesive,protective colloid for PVAc emulsion,suspending agent for PVC, PS polymerization,office glue,tackifier,binder for monitor pigment coating. |
| BP-26 | 50-58 | 86-89 | <5 | <0.5 | 5-7 | |
| BP-24 | 44-50 | 86-89 | <5 | <0.5 | 5-7 | |
| BP-20H | 27-33 | 90-93 | <5 | <0.5 | 5-7 | Warp sizing agent for T/C,polyester spun yarn,protective colloid for PVAc(BP-20LApplication is same as BP-20,only particle is larger) |
| BP-20 | 27-33 | 86-89 | <5 | <0.5 | 5-7 | |
| BP-20L | 27-33 | 86-89 | <5 | <0.5 | 5-7 | |
| BP-20A | 27-33 | 86-89 | <5 | <0.5 | 5-7 | Specification is same as BP-20,and with better defoaming property. |
| BP-17 | 21-26 | 86-89 | <5 | <0.5 | 5-7 | For emulsion,remoistenable adhesive,facial mask,hand cleaner,PVA film,and screen printing photographic film. (BP- 17Lis with larger size of particle) |
| BP-17L | 21-26 | 86-89 | <5 | <0.5 | 5-7 | |
| BP-17A | 21-26 | 86-89 | <5 | <0.5 | 5-7 | Better defoaming property. |
| BP-17N | 21-26 | 86-89 | <5 | <0.5 | 5-7 | Higher transparency. |
| BP-1785 | 21-26 | 82-86 | <5 | <0.5 | 5-7 | Specification is same as BP-17,with lower hydrolysis |
| BP-10H | 9-11 | 90-93 | <5 | <0.5 | 5-7 | Protective colloid for PVAc emulsion ,viscosity modifier for warp sizing agent |
| BP-05 | 5-6 | 86-89 | <5 | <0.5 | 5-7 | Warp sizing agent for filament yarn,protective colloid for PVAc Emulsion,binder for pigmented coating of art paper, remoistenableadhesive,photosensitive film of lithographic printing plate. |
| BP-05A | 5-6 | 86-89 | <5 | <0.5 | 5-7 | Specification is the same as BP-05,and with better defoaming property. |
| BP-05G | 5-6 | 86-89 | <5 | <0.3 | 5-7 | Low content of ash. |
| BP-04 | 4-5 | 86-89 | <5 | <0.5 | 5-7 | High solid content adhesive,remoistenable adhesive, protective colloid for PVAc emulsion,photosensitive film of lithographic printing plate. |
| BP-04N | 4-5 | 86-89 | <5 | <0.5 | 5-7 | Higher transparency compared with BP04. |
| Grade | Viscosity (cps) | Hydrolysis (mole %) | Volatile (wt%) | Ash (wt%) | pH | Application |
|---|---|---|---|---|---|---|
| BF-26 | 70-80 | 98.5-99.2 | <5 | <0.7 | 5-7 | Adhesive,protective colloid for PVAc emulsion,paper surface sizing,stiffen agent for textile. |
| BF-24 | 58-68 | 98.5-99.2 | <5 | <0.7 | 5-7 | |
| BF-20 | 36-42 | 98.5-99.2 | <5 | <0.7 | 5-7 | |
| BF-17H | 25-30 | 99.4-99.8 | <5 | <0.7 | 5-7 | For vinylon fiber manufacturing. |
| BF-17 | 25-30 | 98.5-99.2 | <5 | <0.7 | 5-7 | Warp sizing agent for cotton or rayon spun yarn,paper surface sizing,color coating binder,adhesive for paper, protective colloid for PVAc emulsion,PVA film, PVA sponge,modifier for thermosetting resin,binder for ferrite,binder for non-woven fabrics. |
| BF-17W | 25-30 | 95-97 | <5 | <0.7 | 5-7 | |
| BF-14 | 13-16 | 98.5-99.2 | <5 | <0.7 | 5-7 | |
| BF-14W | 13-16 | 98.5-99.2 | <5 | <0.7 | 5-7 | |
| BF-05 | 5-6 | 98.5-99.2 | <5 | <0.7 | 5-7 | Color coating binder,protective colloid for PVAc emulsion, mold release agent,PVA sponge,modified PVA,PVB |
| Grade | Specification | Application |
|---|---|---|
| BP-05S | Specification is same as BP-05,and with particle pass 80 mesh screen | S-series is specially designed for cement additives and building industry.They improve plaster properties such as flexibility,water retention,and increase plaster viscosity as well.In addition,they do not only reduce the friction of plaster but also enhance its working capacity and quality. (prevent cracking and shedding of plaster,increase adhesion and smoothness of cement.)To mix desired amount of PVA with cement well before water is added prevents the lumping of PVA. |
| BP-17S | Specification is same as BP-17,and with particle pass 80 mesh screen | |
| BP-24S | Specification is same as BP-24,and with particle pass 80 mesh screen |